物性
主要特性 |
|
|---|---|
| Density | 0.924 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 20 |
アプリケーションの利点 |
|
|---|---|
| Anti-block | No |
| Slip | No |
代表的な物性 |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D790B) in MPa (psi) | 386 (56000) |
| 2% Secant Modulus, TD (ASTM D790B) in MPa (psi) | 386 (56000) |
| Enhanced LLDPE | No |
| Fabrication Method | Injection Molding |
| Functionality | Mechanical Performance |
| Melting Point, DSC (Dow Method) in °C(°F) | 123 (253) |
| Structure Type | Monolayer, Multilayer |
| Vicat Softening Point in °C(°F) | 93.9 (201) |