2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
560 (81300) ASTM D882
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
632 (91700) ASTM D882
|
|
Brittleness Temperature in °C(°F)
|
<-76.1
|
|
Density Range
|
.951-.960
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
22 hr
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
84.1 kJ/m2 (40 ft lb/in2) ASTM D1822
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
.662(8)
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
690 %
|
|
Tensile Elongation at Break, TD
|
940 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
45.7 (6630) ASTM D882
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
38.9 (5640) ASTM D882
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
24.2 (3510) ASTM D882
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
20.7 (3010) ASTM D882
|