2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1300 (188000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1300 (188000)
|
|
Brittleness Temperature in °C(°F)
|
< -76.1
|
|
Density Range
|
.961+
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
20 hr
|
|
Fabrication Method
|
Sheet Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
84 kJ/m2 (40 ft lb/in2) ASTM D1822
|
|
Tensile Elongation at Break, MD
|
1000 %
|
|
Tensile Elongation at Break, TD
|
1000 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
24 (3480)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
24 (3480)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
32 (4640)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
32 (4640)
|