物性

主要特性

Density 0.923 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 35

アプリケーションの利点

Anti-block No
Slip No
Use Flooring

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 296 (43000) (ASTM D790)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 296 (43000) (ASTM D790)
Fabrication Method Injection Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 252 kJ/m2 (120 ft lb/in2) ASTM D1822
Melting Point, DSC (Dow Method) in °C(°F) 112 (234)
Tensile Elongation at Break, MD 90 (ASTM D638) %
Tensile Elongation at Break, TD 90 (ASTM D638) %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 6.89 (1000) (ASTM D638)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 6.89 (1000) (ASTM D638)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 9.65 (1400) (ASTM D638)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 9.65 (1400) (ASTM D638)
Vicat Softening Point in °C(°F) 95 (203)