物性

主要特性

Density 0.958 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 5

アプリケーションの利点

Anti-block No
Slip No

製品の使用と処方

Type Breathable Cast Film, Non-Breathable Cast Film

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 472 (68500) ASTM D882
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 672 (97500) ASTM D882
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 44 hr
Fabrication Method Cast Film Extrusion, Injection Molding
Functionality Mechanical Performance
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 3.31 (40)
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 600 %
Tensile Elongation at Break, TD 650 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 36 (5220) ASTM D882
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 28 (4060) ASTM D882
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 27 (3920) ASTM D882
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 28 (4060) ASTM D882