物性

主要特性

Density 0.958 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 27
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.28

アプリケーションの利点

Anti-block No
Slip No

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1170 (170000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1170 (170000)
Brittleness Temperature in °C(°F) -60
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (10% IGEPAL) 220 hr
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) > 1100 hr
Fabrication Method Blow Molding, Compression Molding
Functionality Mechanical Performance
Tensile Elongation at Break, MD 800 %
Tensile Elongation at Break, TD 800 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 29 (4210)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 29 (4210)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 24.8 (3600)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 24.8 (3600)