物性

app.properties.Title

Anti-block No
High Hot Tack No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 149 (21600)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 147 (21300)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 66
Density .918 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 37
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 370
Enhanced LLDPE No
Fabrication Method Cast Film Extrusion
Functionality Mechanical Performance
Haze (ASTM D1003) .560 %
Melting Point, DSC (Dow Method) in °C(°F) 116 (241)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 9.02 (109)
Tensile Elongation at Break, MD 450 %
Tensile Elongation at Break, TD 680 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 39.6 (5740)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 20.6 (2990)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10.7 (1550)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 8.96 (1300)
Vicat Softening Point in °C(°F) 96.1 (205)