2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
120 (17400)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
135 (19600)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
850 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
690 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
850 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Flow Index (g/10 min)
|
1
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
8 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
190 to 240 (374 to 464)
|
|
Tensile Elongation at Break, MD
|
640 - 1.6 mil (40 µm) %
|
|
Tensile Elongation at Break, TD
|
760 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
31.0 (4500)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
30.0 (4350)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
6.50 (943)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
6.20 (899)
|
|
Vicat Softening Point in °C(°F)
|
92.0 (198)
|