物性

主要特性

Density 0.912 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.80

アプリケーションの利点

Anti-block No
Slip No

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 124 (18000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 131 (19000)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 380 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 250 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 600 g
Fabrication Method Blown Film Extrusion, Oriented (Biaxially), Sheet Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Gloss (45 degree) 49
Haze (ASTM D1003) 11 %
Melting Point, DSC (Dow Method) in °C(°F) 101 (214)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 33.1 (400)
Tensile Elongation at Break, MD 400 %
Tensile Elongation at Break, TD 450 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 41.4 (6000)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 37.2 (5400)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 8.96 (1300)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 8.62 (1250)
Vicat Softening Point in °C(°F) 99 (210)