2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
138 (20000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
141 (20500)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
870 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
370 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
590 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Gloss (45 degree)
|
33
|
|
Haze (ASTM D1003)
|
1.7 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
123 (253)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
31.4 (380)
|
|
Tensile Elongation at Break, MD
|
520 %
|
|
Tensile Elongation at Break, TD
|
710 - 1.0 mil (25 µm) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
38.5 (5580)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
34.4 (4990)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.1 (1460)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
9.03 (1310)
|
|
Vicat Softening Point in °C(°F)
|
92.8 (199)
|