物性

アプリケーションの利点

Anti-block No
Slip false
Tie Layers No

代表的な物性

Density 0.902 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 550 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 720 g
Fabrication Method Blown Film Extrusion, Foam Extrusion, Sheet Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Haze (ASTM D1003) 1.1 %
Heat Seal Initiation Temp in °C(°F) 85 (185)
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 1, 1
Melting Point, DSC (Dow Method) in °C(°F) 99 (210)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 22.3 (270 )
Structure Type Multilayer
Tensile Elongation at Break, MD 620 %
Tensile Elongation at Break, TD 630 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 58.6 (8500)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 44.7 (6480)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 7.24 (1050)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 6.89 (1000)
Vicat Softening Point in °C(°F) 86 (187)