物性

app.properties.Title

Anti-block No
Slip false

typical.properties.Title

Density 0.91 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 180 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 360 g
Fabrication Method Cast Film Extrusion
Functionality Sealant (non-peelable)
Haze (ASTM D1003) 0.7 %
Heat Seal Initiation Temp in °C(°F) 99 (210)
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 3.5
Melting Point, DSC (Dow Method) in °C(°F) 103 (217)
Tensile Elongation at Break, MD 530 %
Tensile Elongation at Break, TD 670 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 45 (6530)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 33 (4790)
Vicat Softening Point in °C(°F) 95 (203)