속성

응용 프로그램 이점

Anti-block No
Slip false

제품 사용 및 배합

Type Breathable Cast Film

대표적 특성

Density 0.867 g/cm3
Fabrication Method Blown Film Extrusion
Haze (ASTM D1003) 4 %
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 8
Melting Point, DSC (Dow Method) in °C(°F) 62 (144)
Tensile Elongation at Break, MD 750 (ASTM D638) %
Tensile Elongation at Break, TD 750 (ASTM D638) %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 19.6 (2480) (ASTM D638)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 19.6 (2480) (ASTM D638)
Vicat Softening Point in °C(°F) 42 (108)