2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1000 (150000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1000 (150000)
|
|
Brittleness Temperature in °C(°F)
|
< -76.1
|
|
Density Range
|
.951-.960
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
50 hr
|
|
Fabrication Method
|
Blow Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
168 kJ/m2 (80 ft lb/in2) ASTM D1822
|
|
Tensile Elongation at Break, MD
|
1000 %
|
|
Tensile Elongation at Break, TD
|
1000 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
31.7 (4600)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
31.7 (4600)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|