2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1160 (16800)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1160 (16800)
|
Brittleness Temperature in °C(°F)
|
< .101
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
8 hr
|
Fabrication Method
|
Injection Molding
|
Functionality
|
Mechanical Performance
|
Impact Strength in MPa (psi)
|
105 kJ/m2 (50 ft lb/in2) ASTM D1822
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
10
|
Structure Type
|
Monolayer, Multilayer
|
Tensile Elongation at Break, MD
|
1200 %
|
Tensile Elongation at Break, TD
|
1200 %
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
18.6 (2700)
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
18.6 (2700)
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
29 (4200)
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
29 (4200)
|