2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
8810 (118000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
948 (138000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
66g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
16g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
350g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
133 (271)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.03 (49.0)
|
|
Tensile Elongation at Break, MD
|
560 %
|
|
Tensile Elongation at Break, TD
|
320 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
31.7 (4600)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
14.8 (2150)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
26.7 (3880)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
26.6 (3860)
|