속성

주요 속성

Density 0.939 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 11

응용 프로그램 이점

Anti-block No
Slip No

대표적 특성

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 798 (116000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 887 (129000)
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance
Impact Strength in MPa (psi) 76 J/m (1.4 ft-lb/in) - Notched Izod Impact (23˚C (73˚F))
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238)) 0.38
Tensile Elongation at Break, MD 310 %
Tensile Elongation at Break, TD 610 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 34.8 (5050)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 26.0 (3770)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 16.0 (2330)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 18.0 (2610)