주요 속성 |
|
|---|---|
| Density | 0.939 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 16 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 15.5 |
응용 프로그램 이점 |
|
|---|---|
| Anti-block | No |
| Slip | No |
대표적 특성 |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 578 (83800) |
| ESCR-Environmental Stress Crack Resistance (100% IGEPAL) | >2000 hr - 100˚C (212˚F) |
| Fabrication Method | Blown Film Extrusion |
| Functionality | Mechanical Performance |
| Tensile Elongation at Break, MD | 630 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 29.0 (4210) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 18.0 (2610) |