2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
211 (30600)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
219 (31800)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
120 g (ISO 7765-1a-/A)
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
230 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
230 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Optical Performance, Processing
|
Tensile Elongation at Break, MD
|
370 %
|
Tensile Elongation at Break, TD
|
530 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
22 (3190)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
20 (2900)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12 (1740)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
13 (1890)
|
Vicat Softening Point in °C(°F)
|
104 (219)
|