Dart Drop Impact (ASTM D1709A) in grams (lbs) 100 g
Density 0.922 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 430 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 390 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 3
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 2 J/cm3 (24.2 ft lb/in3)
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 550 %
Tensile Elongation at Break, TD 750 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 50 (2900)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 15 (2180)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 11 (1600)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)