Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
240 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
190 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
220 g
|
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.3
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
5 J/cm3 (60.4 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
420 %
|
|
Tensile Elongation at Break, TD
|
680 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
23 (3340)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
18 (2610)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10 (1450)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10 (1450)
|