key.properties.Title |
|
---|---|
Density | 0.921 g/cm3 |
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.25 |
app.properties.Title |
|
---|---|
Anti-block | No |
Collation Shrink Usage | Logistics, Retail |
Slip | No |
Tie Layers | No |
typical.properties.Title |
|
---|---|
Dart Drop Impact (ASTM D1709A) in grams (lbs) | 190 g |
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 300 g |
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 180 g |
Fabrication Method | Blown Film Extrusion, Blown Film Extrusion |
Functionality | Processing |
Gloss (45 degree) | 50 |
Haze (ASTM D1003) | 11 % |
Tensile Elongation at Break, MD | 470 % |
Tensile Elongation at Break, TD | 660 % |
Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 31.8 (4610) |
Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 28.9 (4190) |
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 12.1 (1750) |
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) | 12.1 (1750) |