2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1000 (145000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1000 (145000)
|
|
Density Range
|
.940-.950
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
13.8 (2000)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
13.8 (2000)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|