속성

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 560 (81300) ASTM D882
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 632 (91700) ASTM D882
Brittleness Temperature in °C(°F) <-76.1
Density 0.952 g/cm3
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 22 hr
Fabrication Method Injection Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 84.1 kJ/m2 (40 ft lb/in2) ASTM D1822
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 4.4
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 4.4
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) .662(8)
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 690 %
Tensile Elongation at Break, TD 940 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 45.7 (6630) ASTM D882
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 38.9 (5640) ASTM D882
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 24.2 (3510) ASTM D882
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 20.7 (3010) ASTM D882