Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
25 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
200 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
100 g
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
80
|
|
Haze (ASTM D1003)
|
4.4 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
113 (235)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
.910 J/cm3 (11 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
150 %
|
|
Tensile Elongation at Break, TD
|
440 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
32.4 (4700)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
12.8 (1850)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
13.9 (2010)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.4 (1660)
|
|
Vicat Softening Point in °C(°F)
|
96.1 (205)
|