2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1310 (190000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1310 (190000)
|
|
Brittleness Temperature in °C(°F)
|
< -73.3
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
158 kJ/m2 (75 ft lb/in2) ASTM D1822
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
200 %
|
|
Tensile Elongation at Break, TD
|
200 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
14.5 (2100)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
14.5 (2100)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
29.6 (4300)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
29.6 (4300)
|