2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
472 (68500) ASTM D882
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
672 (97500) ASTM D882
|
|
Density Range
|
.951-.960
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
44 hr
|
|
Fabrication Method
|
Cast Film Extrusion, Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
3.31 (40)
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
600 %
|
|
Tensile Elongation at Break, TD
|
650 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
36 (5220) ASTM D882
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
28 (4060) ASTM D882
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
27 (3920) ASTM D882
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
28 (4060) ASTM D882
|