2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
150 (21800)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
145 (21000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
140
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
220
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
330
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
53
|
|
Haze (ASTM D1003)
|
13 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
116 (241)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
5 (60.4)
|
|
Tensile Elongation at Break, MD
|
950 %
|
|
Tensile Elongation at Break, TD
|
1100 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
33 (4790)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
25 (3630)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10 (1450)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10 (1450)
|
|
Vicat Softening Point in °C(°F)
|
96.7 (206)
|