2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
194 (28100)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
174 (25200)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
50
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
52
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
260
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
93
|
|
Haze (ASTM D1003)
|
.940 %
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
11.1 (134)
|
|
Tensile Elongation at Break, MD
|
560 %
|
|
Tensile Elongation at Break, TD
|
870 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
6.00 (870)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
5.20 (754)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
33.6 (4870)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
18.1 (2630)
|