속성
key.properties.Title |
|
---|---|
Density | 0.919 g/cm3 |
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.22 |
app.properties.Title |
|
---|---|
Anti-block | No |
Collation Shrink Usage | Logistics, Retail |
Slip | No |
Tie Layers | No |
typical.properties.Title |
|
---|---|
2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 200 (29000) |
2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 228 (33000) |
Dart Drop Impact (ASTM D1709A) in grams (lbs) | 170 g |
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 220 g |
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 210 g |
Fabrication Method | Blown Film Extrusion, Blown Film Extrusion |
Functionality | Processing |
Gloss (45 degree) | 34 |
Haze (ASTM D1003) | 18 % |
Melting Point, DSC (Dow Method) in °C(°F) | 109 (228) |
Tensile Elongation at Break, MD | 220 % |
Tensile Elongation at Break, TD | 500 % |
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 11 (1600) |
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) | 11 (1600) |