Density
|
0.87 g/cm3
|
|
Fabrication Method
|
Compounding and Blending
|
|
Functionality
|
Sealant (non-peelable)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
1000
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
67.8 (154)
|
|
Tensile Elongation at Break, MD
|
110 %
|
|
Tensile Elongation at Break, TD
|
110 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
1.55 (225) ASTM D638 (not at break)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
1.55 (225) ASTM D638 (not at break)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
1.55 (225) ASTM D638 (not at yield)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
1.55 (225) ASTM D638 (not at yield)
|
|
Viscosity (350°F)
|
8195 cP
|