2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
2 mil - 201 (29200)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
2 mil - 227 (32900)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
2 mil - 120 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
2 mil - 400 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
2 mil - 450 g
|
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
71
|
|
Haze (ASTM D1003)
|
2 mil - 7 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
112 (234)
|
|
Tensile Elongation at Break, MD
|
2 mil - 370 %
|
|
Tensile Elongation at Break, TD
|
2 mil - 570 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
2 mil - 21.6 (3130)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
2 mil - 16.9 (2450)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
2 mil - 11.8 (1710)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
2 mi - 12.2 (1770)
|
|
Vicat Softening Point in °C(°F)
|
97.2 (207)
|