Density 0.905 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 1

Anti-block No
Slip No
Tie Layers No

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 90.0 (13100)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 95.0 (13800)
Dart Drop Impact (ASTM D1709A) in grams (lbs) >850 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 660 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 800 g
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Haze (ASTM D1003) 7 %
Melting Point, DSC (Dow Method) in °C(°F) 190 to 240 (374 to 464)
Tensile Elongation at Break, MD 670 - 1.6 mil (40 µm) %
Tensile Elongation at Break, TD 790 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 33.0 (4790)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 30.0 (4350)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 5.70 (827)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 5.40 (783)
Vicat Softening Point in °C(°F) 84.0 (183)