VORAFORCE™ TP 1200 NA Isocyanate

O que é VORAFORCE™ TP 1200 NA Isocyanate?

Used in combination with VORAFORCE™ TP 1264 Formulated Polyol to deliver a two-component polyurethane resin system that allows for the manufacturing of composites made via pultrusion. The resulting composites possess characteristically high glass fiber content (~82wt%), superior strength and toughness compared to traditional polyester, vinyl ester and epoxies and fast production line speeds.

Usos

Building solutions: Thermally insulating, durable door and window systems with improved fire ratings
Utility infrastructure: Self-extinguishing utility poles, corrosion-free cross-arms, insulators and arrestors
Transportation: Light weight, cost-effective components for trucks, passenger vehicles and railways
Marine infrastructure: Weather-resistant bridges, decking, seawalls and piling
Storage: High load bearing, cost-effective structural containers, trays and shelving
Renewable energy: Corrosion-free, flame-retardant solar panel frames, defect-free & low-cost wind blade spar caps
Aerospace: Consistently high-quality aircraft frames, beams and structures with self-extinguishing

Benefícios

Low mix viscosity to facilitate adequate wet-out for profiles up to 0.50 to 0.75-inches thick
High glass-fiber loading (~82wt%) enables low-cost and thinner part thicknesses
100% free of styrene, diluents and other high VOC solvents common for polyesters and vinyl esters
Increased strength and impact toughness vs. polyester, vinyl ester and epoxy
Several times the pultrusion line speed of epoxy resin pultrusion
Supplied with or without pre-blended internal mold release
Available in black color under VORAFORCE™ TP1291 Polyol
High surface quality with excellent paint & coating adhesion
Self-extinguishing composites with ASTM E84 Class A fire rating

Propriedades

Propriedades típicas
2K resin components	Formulated polyol (includes mold release) and isocyanate
Appearance	Natural or black pre-pigmented
Density	2.1 kg/m3
Dielectric Strength	(ASTM D149): Greater than 30 kV/mm
Fiber loading	Up to 84 wt%
Gel time	25-35 minutes
Longitudinal flexural modulus	(80wt% glass rovings): Greater than 50 GPa in accordance with ASTM D790
Mixing Viscosity	Mix Viscosity at 23°C = 200 – 400 cP
Self-extinguishing fire performance	ASTM E84 Class A
Tg-Glass Transition Temp	Greater than 130-140°C