Propriedades
Benefícios da Aplicação |
|
|---|---|
| Anti-block | No |
| Slip | false |
Uso e formulação do produto |
|
|---|---|
| Type | Breathable Cast Film |
Propriedades típicas |
|
|---|---|
| Density | 0.867 g/cm3 |
| Fabrication Method | Blown Film Extrusion |
| Haze (ASTM D1003) | 4 % |
| Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) | 8 |
| Melting Point, DSC (Dow Method) in °C(°F) | 62 (144) |
| Tensile Elongation at Break, MD | 750 (ASTM D638) % |
| Tensile Elongation at Break, TD | 750 (ASTM D638) % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 19.6 (2480) (ASTM D638) |
| Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 19.6 (2480) (ASTM D638) |
| Vicat Softening Point in °C(°F) | 42 (108) |