2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
552 (80000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
745 (108000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
< 50 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
16 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1200 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
21
|
|
Haze (ASTM D1003)
|
35 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
125 (257)
|
|
Vicat Softening Point in °C(°F)
|
118 (245)
|