2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
435 (63100)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
432 (62700)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
280 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
120 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
570 g
|
Enhanced LLDPE
|
Yes
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Gloss (45 degree)
|
24
|
Haze (ASTM D1003)
|
30 %
|
Melting Point, DSC (Dow Method) in °C(°F)
|
125 (257)
|
Vicat Softening Point in °C(°F)
|
123 (253)
|