2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
178 (25800)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
203 (29400)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
600 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
740 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
890 g
|
Enhanced LLDPE
|
No
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance, Optical Performance
|
Gloss (45 degree)
|
63
|
Haze (ASTM D1003)
|
11.4 %
|
Melting Point, DSC (Dow Method) in °C(°F)
|
121 (250)
|
Vicat Softening Point in °C(°F)
|
108 (226)
|