2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
204 (29600)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
223 (32400)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
180 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
350 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
710 g
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
26
|
|
Haze (ASTM D1003)
|
25 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
119 (246)
|
|
Vicat Softening Point in °C(°F)
|
109 (228)
|