Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
150 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
280 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
350 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.7
|
Melting Point, DSC (Dow Method) in °C(°F)
|
112 (234)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.96 J/cm3 (60 ft lb/in3)
|
Tensile Elongation at Break, MD
|
480 %
|
Tensile Elongation at Break, TD
|
680 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
29.7 (4310)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
28.4 (4120)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12.6 (1830)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.4 (1660)
|
Vicat Softening Point in °C(°F)
|
97.8 (208)
|