Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
280 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
200 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
170 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance, Optical Performance
|
|
Gloss (45 degree)
|
62
|
|
Haze (ASTM D1003)
|
10 %
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
6 J/cm3 (72.5 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
360 %
|
|
Tensile Elongation at Break, TD
|
720 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
25 (3630)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
25 (3630)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10 (1450)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|