Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238))
|
11
|
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238))
|
0.36
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.96 (60)
|
Tensile Elongation at Break, MD
|
260 %
|
Tensile Elongation at Break, TD
|
530 %
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
49.9 (7240) ASTM D882
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
33 (4780) ASTM D882
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
31 (4500) ASTM D882
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
28 (4060) ASTM D882
|