2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1050 (152000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1050 (152000)
|
|
Density Range
|
.951-.960
|
|
ESCR-Environmental Stress Crack Resistance (10% IGEPAL)
|
12 hr
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
22 hr
|
|
Fabrication Method
|
Compression Molding, Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Tensile Elongation at Break, MD
|
1500 %
|
|
Tensile Elongation at Break, TD
|
1500 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
20.5 (2970)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
20.5 (2970)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
27.3 (3960)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
27.3 (3960)
|