2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
576 (83500)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
576 (83500)
|
|
Brittleness Temperature in °C(°F)
|
-52.8
|
|
Density Range
|
.940-.950
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
6 hr
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
90.4 kJ/m2 (43 ft lb/in2) ASTM D1822
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
37 %
|
|
Tensile Elongation at Break, TD
|
37 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
14.4 (2090)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
14.4 (2090)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
20.9 (3030)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
20.9 (3030)
|