2% Secant Modulus, MD (ASTM D790B) in MPa (psi)
|
1300
|
|
Brittleness Temperature in °C(°F)
|
< -76.1 °C
|
|
DTUL (0.45 MPa, Unannealed)
|
76.1 °C
|
|
Hardness, Shore D
|
66
|
|
Melting Point in °C(°F)
|
133 °C
|
|
Peak Crystallization Temperature
|
120 °C
|
|
Tensile Elongation at Break, MD
|
1000 %
|
|
Tensile Elongation at Yield, MD
|
7.0 %
|
|
Tensile Impact Strength, Type S
|
84.1 kJ/m2
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
24.1 MPa
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
31.7 MPa
|
|
Vicat Softening Point in °C(°F)
|
131 °C
|