Propriedades

app.properties.Title

Anti-block Yes
Collation Shrink Usage Logistics, Retail
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 2 mil - 201 (29200)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 2 mil - 227 (32900)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 2 mil - 120 g
Density 0.924 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 2 mil - 400 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 2 mil - 450 g
Fabrication Method Blown Film Extrusion, Blown Film Extrusion
Functionality Mechanical Performance
Gloss (45 degree) 71
Haze (ASTM D1003) 2 mil - 7 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.88
Melting Point, DSC (Dow Method) in °C(°F) 112 (234)
Tensile Elongation at Break, MD 2 mil - 370 %
Tensile Elongation at Break, TD 2 mil - 570 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 2 mil - 21.6 (3130)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 2 mil - 16.9 (2450)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 2 mil - 11.8 (1710)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 2 mi - 12.2 (1770)
Vicat Softening Point in °C(°F) 97.2 (207)