2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1070 (155000) ASTM D638
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1070 (155000) ASTM D638
|
Brittleness Temperature in °C(°F)
|
< -76.1
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
12 hr
|
Fabrication Method
|
Injection Molding
|
Functionality
|
Mechanical Performance
|
Impact Strength in MPa (psi)
|
84.1 kJ/m2 (40 ft lb/in2) ASTM D1822
|
Structure Type
|
Monolayer, Multilayer
|
Tensile Elongation at Break, MD
|
1100 %
|
Tensile Elongation at Break, TD
|
1100 %
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
23.4 (3400)
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
23.4 (3400)
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
26.9 (3900)
|