2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1110 (160000) ASTM D638
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1110 (160000) ASTM D638
|
|
Density Range
|
.951-.960
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
3 hr
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
670 %
|
|
Tensile Elongation at Break, TD
|
670 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
17 (2470)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
17 (2470)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
29 (4200)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
29 (4200)
|