2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
183 (26600)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
217 (31500)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
100
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
110
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
260
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Haze (ASTM D1003)
|
11 %
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
8.19 (99.0)
|
|
Tensile Elongation at Break, MD
|
660 %
|
|
Tensile Elongation at Break, TD
|
710 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
10.3 (1500)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
25.0 (3630)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.3 (1500)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.0 (1600)
|
|
Vicat Softening Point in °C(°F)
|
101 (214)
|