2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
124 (18000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
131 (19000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
380 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
250 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
600 g
|
|
Fabrication Method
|
Blown Film Extrusion, Oriented (Biaxially), Sheet Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Gloss (45 degree)
|
49
|
|
Haze (ASTM D1003)
|
11 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
101 (214)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
33.1 (400)
|
|
Tensile Elongation at Break, MD
|
400 %
|
|
Tensile Elongation at Break, TD
|
450 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
41.4 (6000)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
37.2 (5400)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
8.96 (1300)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
8.62 (1250)
|
|
Vicat Softening Point in °C(°F)
|
99 (210)
|